琥珀色聚酰胺热熔胶。对多孔基材具有良好的附着力，例如：纸张、木材和皮革。


TECHNOMELT PA 6812是一种用于一般组装应用的琥珀色聚酰胺热熔胶粘剂。该产品通过自然放置在热塑性条件下进行固化。
TECHNOMELT PA 6812特别适用于多孔基材，例如：纸张、木材和皮革。施胶温度范围+437 °F至+464 °F（+225 ℃至+240 ℃）。


·适用于多孔基材，例如：纸张、木材和皮革
·通过自然放置在热塑性条件下进行固化




PRODUCT DESCRIPTION
MACROMELT 6812 provides the following product
characteristics:




Technology : Polyamide
Product Type : Hotmelt
Cure : Physical setting
Condition : Thermoplastic
Components : One component
Application : General assembly
Appearance : Amber


Application Areas
MACROMELT 6812 is a hotmelt adhesive especially
suitable for porous substrates such as paper, wood andleather.


TECHNICAL DATA
Macromelt 6812:
Softening point, ℃ 206 to 216
Melting Viscosity at 235 ℃, mPas 4,000 to 7,500
Specific gravity, g/cm3 0.98
Yield Strength, N/mm 21
Break Strength, N/mm 17
Elongation, % 300
E-modulus 2%, N/mm2 350
Mandrel test ** pass, ℃ 5

DIRECTIONS FOR USE
Preliminary Statement:
Prior to application it is necessary to read the Material
Safety Data Sheet for information about precautionary
measures and safety recommendations. Also, for chemical
products exempt from compulsory labeling, the relevant
precautions should always be observed.


Preparation:
The surfaces of the substrate must be dry and free from oil,
grease and dust.


Application:
Application Temperature : 225 to 240 ℃
Application System : Hotmelt application systems
nourde polyamide low pressure molding


When bonding to a substrate with high thermal conductivity
the use of a specific application temperature is required for
good wetting.


Do not heat the product above the specified application
temperature range.
When the product is not in use do not apply heat, this will
degrade the quality of the product and in extreme cases
cause carbonisation. The standby temperature for the
product is approximately 50℃ below the application
temperature, but not for longer than 72 hours.
MACROMELT 6812 may absorb moisture from the air. This
will not be apparent in the solid form, but may cause
bubbles on heating and could affect the bond quality. It is
important, therefore, that containers are kept closed and
sealed when not in use.


Cleaning:
Carbonised and set (non thermoplastic) material must be
removed mechanically. Removal of the thermoplastic
material from the hot apparatus can be achieved with
solvent free cleaning system, such as Macromelt 0062
(see separate technical information)


Classification:
Please refer to the corresponding safety data sheets for
details on:
  Hazardous Information
  Transport Regulations
  Safety Regulations


Storage:
When properly stored in a cool, dry location, with the
container tightly closed when not in use, this product will
have a shelf life of at least 24 months.
nourde low pressure molding material solutions




ADDITIONAL INFORMATION
Disclaimer:
The information provided herein, especially
recommendations for the usage and the application of our
products, is based upon our knowledge and experience.
Due to different materials used as well as to varying
working conditions beyond our control we strictly
recommend to carry out intensive trials to test the suitability
of our products with regard to the required processes and
applications. We do not accept any liability with regard to
the above information or with regard to any verbal
recommendation, except for cases where we are liable of
gross negligence or false intention.

This datasheet replaces all former versions.